IS 1570 (Part 5) X04Cr17Ni12Mo2 vs IS 1570 (Part 7) 12Cr12MoH

Minimal Match — 39.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) and IS 1570 (Part 7) 12Cr12MoH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr12MoH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X04Cr17Ni12Mo2 vs IS 1570 (Part 7) 12Cr12MoH is a 59.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 39.9%.

Frequently Compared With IS 1570 (Part 5) X04Cr17Ni12Mo2:
ASTM A959 16-8-2H EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
59.9%
MECHANICAL MATCH
0%
OVERALL
39.9%
Specifications
Property IS 1570 (Part 5) X04Cr17Ni12Mo2 IS 1570 (Part 7) 12Cr12MoH
Standard IS 1570 (Part 5):1985 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08-0.16
Si (%) <=1.0 <=0.60
Mn (%) <=2.0 0.40-1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.035
Cr (%) 16.0-18.0 11.5-13.00
Ni (%) 10.0-14.0 <=1.0
Mo (%) 2.0-3.0 0.40-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr17Ni12Mo2 IS 1570 (Part 7) 12Cr12MoH
Tensile Strength >=515 MPa 680-880 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=490 MPa (0.2 % proof stress)
Elongation >=40% (50 mm) >=20%
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Bars, forgings, Q+T, thickness up to 75 (first row of Table 3)
Typical Applications
IS 1570 (Part 5) X04Cr17Ni12Mo2
Not documented
IS 1570 (Part 7) 12Cr12MoH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can IS 1570 (Part 5) X04Cr17Ni12Mo2 Be Substituted With IS 1570 (Part 7) 12Cr12MoH?
IS 1570 (Part 5) X04Cr17Ni12Mo2 and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr17Ni12Mo2 and IS 1570 (Part 7) 12Cr12MoH?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X04Cr17Ni12Mo2 be substituted with IS 1570 (Part 7) 12Cr12MoH?
IS 1570 (Part 5) X04Cr17Ni12Mo2 and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.