IS 1570 (Part 5) X04Cr17Ni12Mo2Ti vs ASTM A276/A276M S31635

Strong Match — 97.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr17Ni12Mo2Ti (IS 1570 (Part 5):1985) and ASTM A276/A276M S31635 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S31635 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X04Cr17Ni12Mo2Ti vs ASTM A276/A276M S31635 is a 96.5% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97.7%.

Frequently Compared With IS 1570 (Part 5) X04Cr17Ni12Mo2Ti:
ASTM A959 16-8-2H EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
96.5%
MECHANICAL MATCH
100%
OVERALL
97.7%
Specifications
Property IS 1570 (Part 5) X04Cr17Ni12Mo2Ti ASTM A276/A276M S31635
Standard IS 1570 (Part 5):1985 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) 10.0-14.0 10.0-14.0
Mo (%) 2.0-3.0 2.00-3.00
Ti (%) <=0.80 <=0.70
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr17Ni12Mo2Ti ASTM A276/A276M S31635
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=205 MPa
Elongation >=40% (50 mm) >=40%
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
Not documented
ASTM A276/A276M S31635
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can IS 1570 (Part 5) X04Cr17Ni12Mo2Ti Be Substituted With ASTM A276/A276M S31635?
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A276/A276M S31635 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31635 is often considered as a substitute for IS 1570 (Part 5) X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
ASTM A276/A276M S31635
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A276/A276M S31635?
ASTM A276/A276M S31635 specifies N which is not specified for IS 1570 (Part 5) X04Cr17Ni12Mo2Ti.
Can IS 1570 (Part 5) X04Cr17Ni12Mo2Ti be substituted with ASTM A276/A276M S31635?
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A276/A276M S31635 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31635 is often considered as a substitute for IS 1570 (Part 5) X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.