IS 1570 (Part 5) X04Cr19Ni13Mo3 vs ASTM A959 317

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr19Ni13Mo3 (IS 1570 (Part 5):1985) and ASTM A959 317 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr19Ni13Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 317 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X04Cr19Ni13Mo3 vs ASTM A959 317 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 5) X04Cr19Ni13Mo3:
GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 12Kh13 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 ASTM A959 317
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 18.0-20.0 18.0-20.0
Ni (%) 11.0-15.0 11.0-15.0
Mo (%) 3.0-4.0 3.0-4.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 ASTM A959 317
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=35% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr19Ni13Mo3
Not documented
ASTM A959 317
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 Be Substituted With ASTM A959 317?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and ASTM A959 317 overlap closely enough on chemistry and mechanical properties that ASTM A959 317 is often considered as a substitute for IS 1570 (Part 5) X04Cr19Ni13Mo3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X04Cr19Ni13Mo3
0 active listings and RFQs →
ASTM A959 317
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr19Ni13Mo3 and ASTM A959 317?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 be substituted with ASTM A959 317?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and ASTM A959 317 overlap closely enough on chemistry and mechanical properties that ASTM A959 317 is often considered as a substitute for IS 1570 (Part 5) X04Cr19Ni13Mo3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.