IS 1570 (Part 5) X04Cr19Ni13Mo3 vs BS 970 (Part 1) 316S33

Close Alternative — 81.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr19Ni13Mo3 (IS 1570 (Part 5):1985) and BS 970 (Part 1) 316S33 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr19Ni13Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 316S33 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 5) X04Cr19Ni13Mo3 vs BS 970 (Part 1) 316S33 is a 81.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.4%.

Frequently Compared With IS 1570 (Part 5) X04Cr19Ni13Mo3:
GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 12Kh13 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
81.4%
MECHANICAL MATCH
No shared data
OVERALL
81.4%
Specifications
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 BS 970 (Part 1) 316S33
Standard IS 1570 (Part 5):1985 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.07
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 18.0-20.0 16.5-18.5
Ni (%) 11.0-15.0 11.0-14.0
Mo (%) 3.0-4.0 2.50-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 BS 970 (Part 1) 316S33
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=35% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr19Ni13Mo3
Not documented
BS 970 (Part 1) 316S33
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 Be Substituted With BS 970 (Part 1) 316S33?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and BS 970 (Part 1) 316S33 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 5) X04Cr19Ni13Mo3
0 active listings and RFQs →
BS 970 (Part 1) 316S33
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr19Ni13Mo3 and BS 970 (Part 1) 316S33?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 be substituted with BS 970 (Part 1) 316S33?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and BS 970 (Part 1) 316S33 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.