IS 1570 (Part 5) X04Cr25Ni20 vs EN 10088-1 1.4401

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr25Ni20 (IS 1570 (Part 5):1985) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr25Ni20 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X04Cr25Ni20 vs EN 10088-1 1.4401 is a 59.7% match. As per mechanical properties, the match is 25%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X04Cr25Ni20:
GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 GOST 5632 12Kh13 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
59.7%
MECHANICAL MATCH
25%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X04Cr25Ni20 EN 10088-1 1.4401
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 ≤0.07
Si (%) <=1.5 ≤1.00
Mn (%) <=2.0 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 24.0-26.0 16.5–18.5
Ni (%) 19.0-22.0 10.5–13.5
Mo (%) Not specified 2.0–2.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr25Ni20 EN 10088-1 1.4401
Tensile Strength >=515 MPa ≥520 MPa
Yield Strength >=205 MPa (0.2 % proof stress) ≥210 MPa
Elongation >=40% (50 mm) ≥40%
Hardness <=217 HB; <=95 HRB ≤215 HB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr25Ni20
Not documented
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can IS 1570 (Part 5) X04Cr25Ni20 Be Substituted With EN 10088-1 1.4401?
IS 1570 (Part 5) X04Cr25Ni20 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X04Cr25Ni20
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X04Cr25Ni20
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr25Ni20 and EN 10088-1 1.4401?
IS 1570 (Part 5) X04Cr25Ni20 specifies P, S which are not specified for EN 10088-1 1.4401. EN 10088-1 1.4401 specifies Mo which is not specified for IS 1570 (Part 5) X04Cr25Ni20.
Can IS 1570 (Part 5) X04Cr25Ni20 be substituted with EN 10088-1 1.4401?
IS 1570 (Part 5) X04Cr25Ni20 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.