IS 1570 (Part 5) X108Cr17Mo vs IS 11169 (Part 2) X04Cr17Ni12Mo2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X108Cr17Mo (IS 1570 (Part 5):1985) and IS 11169 (Part 2) X04Cr17Ni12Mo2 (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X108Cr17Mo is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 2) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X108Cr17Mo vs IS 11169 (Part 2) X04Cr17Ni12Mo2 is a 72.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 5) X108Cr17Mo:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13
Match Breakdown
CHEMISTRY MATCH
72.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 5) X108Cr17Mo IS 11169 (Part 2) X04Cr17Ni12Mo2
Standard IS 1570 (Part 5):1985 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 <=0.08
Si (%) <=1.0 <=1.0
Mn (%) <=1.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) <=0.50 10.0-14.0
Mo (%) <=0.75 2.0-3.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X108Cr17Mo IS 11169 (Part 2) X04Cr17Ni12Mo2
Hardness <=269 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Quenched reference test piece (Table 6 treatment)
Yield Strength (0.2% proof) Not specified >=205 MPa
Tensile Strength Not specified 500-700 MPa
Elongation Not specified >=45%
Impact (U-notch 5 mm) Not specified >=60 J
Typical Applications
IS 1570 (Part 5) X108Cr17Mo
Not documented
IS 11169 (Part 2) X04Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Can IS 1570 (Part 5) X108Cr17Mo Be Substituted With IS 11169 (Part 2) X04Cr17Ni12Mo2?
IS 1570 (Part 5) X108Cr17Mo and IS 11169 (Part 2) X04Cr17Ni12Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X108Cr17Mo
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X108Cr17Mo and IS 11169 (Part 2) X04Cr17Ni12Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X108Cr17Mo be substituted with IS 11169 (Part 2) X04Cr17Ni12Mo2?
IS 1570 (Part 5) X108Cr17Mo and IS 11169 (Part 2) X04Cr17Ni12Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.