IS 1570 (Part 5) X15Cr24Ni13 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr24Ni13 (IS 1570 (Part 5):1985) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr24Ni13 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X15Cr24Ni13 vs GOST 5632 08X18H10 is a 64.9% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X15Cr24Ni13:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 EN 10088-1 1.4006 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4845 GOST 5632 12Kh13 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
64.9%
MECHANICAL MATCH
33.3%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X15Cr24Ni13 GOST 5632 08X18H10
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.20 ≤0.08
Si (%) <=1.5 ≤0.80
Mn (%) <=2.0 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 22.0-25.0 17.0–19.0
Ni (%) 11.0-15.0 9.0–11.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr24Ni13 GOST 5632 08X18H10
Tensile Strength >=490 MPa ≥520 MPa
Yield Strength >=210 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=40% (50 mm) ≥40%
Hardness <=223 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X15Cr24Ni13
Not documented
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Can IS 1570 (Part 5) X15Cr24Ni13 Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 5) X15Cr24Ni13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X15Cr24Ni13
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 5) X15Cr24Ni13
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr24Ni13 and GOST 5632 08X18H10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X15Cr24Ni13 be substituted with GOST 5632 08X18H10?
IS 1570 (Part 5) X15Cr24Ni13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.