Related Material — 68% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X53Cr22Mn9Ni4N (IS 1570 (Part 5):1985) and ASTM A276/A276M S21900 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X53Cr22Mn9Ni4N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S21900 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X53Cr22Mn9Ni4N vs ASTM A276/A276M S21900 is a 68% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68%.

Frequently Compared With IS 1570 (Part 5) X53Cr22Mn9Ni4N:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
68%
MECHANICAL MATCH
No shared data
OVERALL
68%
Specifications
Property IS 1570 (Part 5) X53Cr22Mn9Ni4N ASTM A276/A276M S21900
Standard IS 1570 (Part 5):1985 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) 0.48-0.58 <=0.08
Si (%) <=0.25 <=1.00
Mn (%) 8.0-10.0 8.0-10.0
P (%) <=0.045 <=0.045
S (%) <=0.035 <=0.030
Cr (%) 20.0-23.0 19.0-21.5
Ni (%) 3.25-4.50 5.5-7.5
N (%) Not specified 0.15-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X53Cr22Mn9Ni4N ASTM A276/A276M S21900
Hardness >=321 HB Not specified
Condition Valve steel, hardened and tempered (Table 6) Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=345 MPa
Elongation Not specified >=45%
Typical Applications
IS 1570 (Part 5) X53Cr22Mn9Ni4N
Not documented
ASTM A276/A276M S21900
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can IS 1570 (Part 5) X53Cr22Mn9Ni4N Be Substituted With ASTM A276/A276M S21900?
IS 1570 (Part 5) X53Cr22Mn9Ni4N and ASTM A276/A276M S21900 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X53Cr22Mn9Ni4N
0 active listings and RFQs →
ASTM A276/A276M S21900
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X53Cr22Mn9Ni4N and ASTM A276/A276M S21900?
ASTM A276/A276M S21900 specifies N which is not specified for IS 1570 (Part 5) X53Cr22Mn9Ni4N.
Can IS 1570 (Part 5) X53Cr22Mn9Ni4N be substituted with ASTM A276/A276M S21900?
IS 1570 (Part 5) X53Cr22Mn9Ni4N and ASTM A276/A276M S21900 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.