IS 1570 (Part 5) X53Cr22Mn9Ni4N vs IS 1570 (Part 5) X55Cr21Mn8Ni2N

Strong Match — 86.1% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X53Cr22Mn9Ni4N (IS 1570 (Part 5):1985) and IS 1570 (Part 5) X55Cr21Mn8Ni2N (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X53Cr22Mn9Ni4N is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 5) X55Cr21Mn8Ni2N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X53Cr22Mn9Ni4N vs IS 1570 (Part 5) X55Cr21Mn8Ni2N is a 79.2% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 86.1%.

Frequently Compared With IS 1570 (Part 5) X53Cr22Mn9Ni4N:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
79.2%
MECHANICAL MATCH
100%
OVERALL
86.1%
Specifications
Property IS 1570 (Part 5) X53Cr22Mn9Ni4N IS 1570 (Part 5) X55Cr21Mn8Ni2N
Standard IS 1570 (Part 5):1985 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) 0.48-0.58 0.50-0.60
Si (%) <=0.25 <=1.0
Mn (%) 8.0-10.0 7.0-9.5
P (%) <=0.045 <=0.045
S (%) <=0.035 <=0.035
Cr (%) 20.0-23.0 20.0-22.0
Ni (%) 3.25-4.50 1.5-2.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X53Cr22Mn9Ni4N IS 1570 (Part 5) X55Cr21Mn8Ni2N
Hardness >=321 HB >=321 HB
Condition Valve steel, hardened and tempered (Table 6) Valve steel, hardened and tempered (Table 6)
Can IS 1570 (Part 5) X53Cr22Mn9Ni4N Be Substituted With IS 1570 (Part 5) X55Cr21Mn8Ni2N?
IS 1570 (Part 5) X53Cr22Mn9Ni4N and IS 1570 (Part 5) X55Cr21Mn8Ni2N overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X55Cr21Mn8Ni2N is often considered as a substitute for IS 1570 (Part 5) X53Cr22Mn9Ni4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X53Cr22Mn9Ni4N
0 active listings and RFQs →
IS 1570 (Part 5) X55Cr21Mn8Ni2N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X53Cr22Mn9Ni4N and IS 1570 (Part 5) X55Cr21Mn8Ni2N?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X53Cr22Mn9Ni4N be substituted with IS 1570 (Part 5) X55Cr21Mn8Ni2N?
IS 1570 (Part 5) X53Cr22Mn9Ni4N and IS 1570 (Part 5) X55Cr21Mn8Ni2N overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X55Cr21Mn8Ni2N is often considered as a substitute for IS 1570 (Part 5) X53Cr22Mn9Ni4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.