IS 1570 (Part 5) X66Cr13 vs ASTM A276/A276M S42000

Strong Match — 85% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X66Cr13 (IS 1570 (Part 5):1985) and ASTM A276/A276M S42000 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X66Cr13 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S42000 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X66Cr13 vs ASTM A276/A276M S42000 is a 85% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85%.

Frequently Compared With IS 1570 (Part 5) X66Cr13:
GOST 5632 08X18H10 GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
85%
MECHANICAL MATCH
No shared data
OVERALL
85%
Specifications
Property IS 1570 (Part 5) X66Cr13 ASTM A276/A276M S42000
Standard IS 1570 (Part 5):1985 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) 0.60-0.72 >=0.15
Si (%) <=0.5 <=1.00
Mn (%) 0.40-1.0 <=1.00
Cr (%) 12.0-14.0 12.0-14.0
P (%) Not specified <=0.040
S (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X66Cr13 ASTM A276/A276M S42000
Hardness Not specified <=241 HB
Condition Not specified Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
IS 1570 (Part 5) X66Cr13
Not documented
ASTM A276/A276M S42000
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can IS 1570 (Part 5) X66Cr13 Be Substituted With ASTM A276/A276M S42000?
IS 1570 (Part 5) X66Cr13 and ASTM A276/A276M S42000 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S42000 is often considered as a substitute for IS 1570 (Part 5) X66Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X66Cr13
0 active listings and RFQs →
ASTM A276/A276M S42000
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X66Cr13 and ASTM A276/A276M S42000?
ASTM A276/A276M S42000 specifies P, S which are not specified for IS 1570 (Part 5) X66Cr13.
Can IS 1570 (Part 5) X66Cr13 be substituted with ASTM A276/A276M S42000?
IS 1570 (Part 5) X66Cr13 and ASTM A276/A276M S42000 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S42000 is often considered as a substitute for IS 1570 (Part 5) X66Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.