IS 1570 (Part 5) X80Cr20Si2Ni1 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X80Cr20Si2Ni1 (IS 1570 (Part 5):1985) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X80Cr20Si2Ni1 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X80Cr20Si2Ni1 vs EN 10088-1 1.4301 is a 63.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X80Cr20Si2Ni1:
GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
63.7%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X80Cr20Si2Ni1 EN 10088-1 1.4301
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.75-0.85 ≤0.07
Si (%) 1.75-2.25 ≤1.00
Mn (%) 0.20-0.60 ≤2.00
P (%) <=0.045 ≤0.045
S (%) <=0.030 ≤0.030
Cr (%) 19.0-21.0 17.5–19.5
Ni (%) 1.20-1.70 8.0–10.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X80Cr20Si2Ni1 EN 10088-1 1.4301
Hardness 255-306 HB ≤215 HB
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥45%
Typical Applications
IS 1570 (Part 5) X80Cr20Si2Ni1
Not documented
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Can IS 1570 (Part 5) X80Cr20Si2Ni1 Be Substituted With EN 10088-1 1.4301?
IS 1570 (Part 5) X80Cr20Si2Ni1 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X80Cr20Si2Ni1
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
IS 1570 (Part 5) X80Cr20Si2Ni1
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X80Cr20Si2Ni1 and EN 10088-1 1.4301?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X80Cr20Si2Ni1 be substituted with EN 10088-1 1.4301?
IS 1570 (Part 5) X80Cr20Si2Ni1 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.