IS 1570 (Part 5) X80Cr20Si2Ni1 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X80Cr20Si2Ni1 (IS 1570 (Part 5):1985) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X80Cr20Si2Ni1 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X80Cr20Si2Ni1 vs GOST 5632 06Kh23N28 is a 62.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X80Cr20Si2Ni1:
GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
62.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X80Cr20Si2Ni1 GOST 5632 06Kh23N28
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.75-0.85 ≤0.06
Si (%) 1.75-2.25 ≤0.80
Mn (%) 0.20-0.60 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 19.0-21.0 22.0–25.0
Ni (%) 1.20-1.70 26.0–29.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X80Cr20Si2Ni1 GOST 5632 06Kh23N28
Hardness 255-306 HB Not specified
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
IS 1570 (Part 5) X80Cr20Si2Ni1
Not documented
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can IS 1570 (Part 5) X80Cr20Si2Ni1 Be Substituted With GOST 5632 06Kh23N28?
IS 1570 (Part 5) X80Cr20Si2Ni1 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X80Cr20Si2Ni1
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X80Cr20Si2Ni1
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X80Cr20Si2Ni1 and GOST 5632 06Kh23N28?
IS 1570 (Part 5) X80Cr20Si2Ni1 specifies P, S which are not specified for GOST 5632 06Kh23N28.
Can IS 1570 (Part 5) X80Cr20Si2Ni1 be substituted with GOST 5632 06Kh23N28?
IS 1570 (Part 5) X80Cr20Si2Ni1 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.