IS 1570 (Part 6) T110Mn4W6Cr4 vs GB/T 1299 3Cr2W8V

Related Material — 61.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T110Mn4W6Cr4 (IS 1570 (Part 6):1996) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T110Mn4W6Cr4 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 1570 (Part 6) T110Mn4W6Cr4 vs GB/T 1299 3Cr2W8V is a 61.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 61.4%.

Frequently Compared With IS 1570 (Part 6) T110Mn4W6Cr4:
EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 EN ISO 683-17 100Cr6 IS 1570 (Part 6) 103T3 GOST 5950 3H2W8F DIN EN ISO 4957 1.2344 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 IS 3748 103T3 IS 3748 118T3
Match Breakdown
CHEMISTRY MATCH
61.4%
MECHANICAL MATCH
No shared data
OVERALL
61.4%
Specifications
Property IS 1570 (Part 6) T110Mn4W6Cr4 GB/T 1299 3Cr2W8V
Standard IS 1570 (Part 6):1996 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 1.00-1.20 0.30-0.40
Si (%) 0.10-0.35 0.20-0.40
Mn (%) 0.90-1.30 0.20-0.50
Cr (%) 0.90-1.30 2.20-2.70
W (%) 1.25-1.75 7.50-9.00
P (%) <=0.035 0.030 max
S (%) <=0.035 0.030 max
V (%) Not specified 0.20-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T110Mn4W6Cr4 GB/T 1299 3Cr2W8V
Tensile Strength Not specified 1180-1380 MPa
Yield Strength Not specified 980-1180 MPa
Elongation Not specified 10-14%
Hardness Not specified 48-54 HRC
Typical Applications
IS 1570 (Part 6) T110Mn4W6Cr4
Not documented
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Key Differences
Can IS 1570 (Part 6) T110Mn4W6Cr4 Be Substituted With GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) T110Mn4W6Cr4 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) T110Mn4W6Cr4
No active listings currently.
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
IS 1570 (Part 6) T110Mn4W6Cr4
0 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T110Mn4W6Cr4 and GB/T 1299 3Cr2W8V?
GB/T 1299 3Cr2W8V specifies V which is not specified for IS 1570 (Part 6) T110Mn4W6Cr4.
Can IS 1570 (Part 6) T110Mn4W6Cr4 be substituted with GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) T110Mn4W6Cr4 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.