IS 1570 (Part 6) XT55W14Cr3V4 vs GB/T 1299 3Cr2W8V

Related Material — 67.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT55W14Cr3V4 (IS 1570 (Part 6):1996) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT55W14Cr3V4 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 1570 (Part 6) XT55W14Cr3V4 vs GB/T 1299 3Cr2W8V is a 67.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.7%.

Frequently Compared With IS 1570 (Part 6) XT55W14Cr3V4:
EN ISO 4957 1.2316 EN ISO 683-17 100Cr6 GOST 5950 3H2W8F GOST 5950 4H5MFS1 DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV1 GB/T 1299 4Cr5MoSiV IS 3748 103T3
Match Breakdown
CHEMISTRY MATCH
67.7%
MECHANICAL MATCH
No shared data
OVERALL
67.7%
Specifications
Property IS 1570 (Part 6) XT55W14Cr3V4 GB/T 1299 3Cr2W8V
Standard IS 1570 (Part 6):1996 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.50-0.60 0.30-0.40
Si (%) 0.10-0.35 0.20-0.40
Mn (%) 0.20-0.40 0.20-0.50
Cr (%) 2.80-3.30 2.20-2.70
V (%) 0.30-0.60 0.20-0.50
W (%) 13.0-15.0 7.50-9.00
P (%) <=0.035 0.030 max
S (%) <=0.035 0.030 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT55W14Cr3V4 GB/T 1299 3Cr2W8V
Tensile Strength Not specified 1180-1380 MPa
Yield Strength Not specified 980-1180 MPa
Elongation Not specified 10-14%
Hardness Not specified 48-54 HRC
Typical Applications
IS 1570 (Part 6) XT55W14Cr3V4
Not documented
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Can IS 1570 (Part 6) XT55W14Cr3V4 Be Substituted With GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) XT55W14Cr3V4 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) XT55W14Cr3V4
No active listings currently.
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
IS 1570 (Part 6) XT55W14Cr3V4
0 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT55W14Cr3V4 and GB/T 1299 3Cr2W8V?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) XT55W14Cr3V4 be substituted with GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) XT55W14Cr3V4 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.