IS 1570 (Part 6) XT55W14Cr3V4 vs GOST 5950 3H2W8F

Related Material — 65.3% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT55W14Cr3V4 (IS 1570 (Part 6):1996) and GOST 5950 3H2W8F (GOST 5950-2000) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT55W14Cr3V4 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 6) XT55W14Cr3V4 vs GOST 5950 3H2W8F is a 65.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.3%.

Frequently Compared With IS 1570 (Part 6) XT55W14Cr3V4:
EN ISO 4957 1.2316 EN ISO 683-17 100Cr6 GB/T 1299 3Cr2W8V DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 GOST 5950 4H5MFS1 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 IS 1570 (Part 6) 103T3 GB/T 1299 4Cr5MoSiV1 GB/T 1299 4Cr5MoSiV IS 3748 103T3
Match Breakdown
CHEMISTRY MATCH
65.3%
MECHANICAL MATCH
No shared data
OVERALL
65.3%
Specifications
Property IS 1570 (Part 6) XT55W14Cr3V4 GOST 5950 3H2W8F
Standard IS 1570 (Part 6):1996 GOST 5950-2000
Category Tool & Die Steels Tool & Die Steels
C (%) 0.50-0.60 0.3-0.4
Si (%) 0.10-0.35 0.2-0.5
Mn (%) 0.20-0.40 Not specified
Cr (%) 2.80-3.30 2.2-2.7
V (%) 0.30-0.60 0.3-0.6
W (%) 13.0-15.0 7.5-9.0
P (%) <=0.035 Not specified
S (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT55W14Cr3V4 GOST 5950 3H2W8F
Tensile Strength Not specified 1400-1700 MPa
Yield Strength Not specified 1200 MPa min
Elongation Not specified 8% min
Hardness Not specified 45-50 HRC
Typical Applications
IS 1570 (Part 6) XT55W14Cr3V4
Not documented
GOST 5950 3H2W8F
Used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.
Key Differences
Can IS 1570 (Part 6) XT55W14Cr3V4 Be Substituted With GOST 5950 3H2W8F?
IS 1570 (Part 6) XT55W14Cr3V4 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) XT55W14Cr3V4
No active listings currently.
GOST 5950 3H2W8F
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–4300 mm (110.24–169.29 in)
On M-EX Right Now
IS 1570 (Part 6) XT55W14Cr3V4
0 active listings and RFQs →
GOST 5950 3H2W8F
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT55W14Cr3V4 and GOST 5950 3H2W8F?
IS 1570 (Part 6) XT55W14Cr3V4 specifies Mn, P, S which are not specified for GOST 5950 3H2W8F.
Can IS 1570 (Part 6) XT55W14Cr3V4 be substituted with GOST 5950 3H2W8F?
IS 1570 (Part 6) XT55W14Cr3V4 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.