Related Material — 65% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) and ASTM A959 XM-34 (ASTM A959:2011) are both steel grades. IS 1570 (Part 7) 10Cr36Mo10H is classified under Alloy Steel, while ASTM A959 XM-34 is classified under Stainless Steel — a different category, which is worth noting alongside the chemistry match below. IS 1570 (Part 7) 10Cr36Mo10H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while ASTM A959 XM-34 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 XM-34 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 10Cr36Mo10H vs ASTM A959 XM-34 is a 70.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With IS 1570 (Part 7) 10Cr36Mo10H:
IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 12Cr4Mo5H IS 1570 (Part 7) 12Cr9Mo10H IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 GB/T 3077 12Cr2Ni4A
Match Breakdown
CHEMISTRY MATCH
70.4%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property IS 1570 (Part 7) 10Cr36Mo10H ASTM A959 XM-34
Standard IS 1570 (Part 7):1992 ASTM A959:2011
Category Alloy Steel Stainless Steel
C (%) <=0.15 <=0.08
Si (%) 0.25-1.0 <=1.00
Mn (%) 0.30-0.60 <=2.50
P (%) <=0.040 <=0.040
S (%) <=0.030 >=0.15
Cr (%) 8.00-10.00 17.5-19.5
Mo (%) 0.90-1.10 1.50-2.50
Al (metallic) (%) <=0.02 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 10Cr36Mo10H ASTM A959 XM-34
Tensile Strength 410-560 MPa Not specified
Yield Strength >=135 MPa (0.2 % proof stress) Not specified
Elongation >=20% Not specified
Condition Pipes, A, thickness - (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
ASTM A959 XM-34
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 7) 10Cr36Mo10H Be Substituted With ASTM A959 XM-34?
IS 1570 (Part 7) 10Cr36Mo10H and ASTM A959 XM-34 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
ASTM A959 XM-34
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 10Cr36Mo10H and ASTM A959 XM-34?
Different category: IS 1570 (Part 7) 10Cr36Mo10H is Alloy Steel, ASTM A959 XM-34 is Stainless Steel. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for ASTM A959 XM-34.
Can IS 1570 (Part 7) 10Cr36Mo10H be substituted with ASTM A959 XM-34?
IS 1570 (Part 7) 10Cr36Mo10H and ASTM A959 XM-34 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.