Related Material — 65.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) and SAE J404 4130 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 7) 10Cr36Mo10H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while SAE J404 4130 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 4130 is defined under SAE International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 10Cr36Mo10H vs SAE J404 4130 is a 65.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.9%.

Frequently Compared With IS 1570 (Part 7) 10Cr36Mo10H:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 12Cr4Mo5H IS 1570 (Part 7) 12Cr9Mo10H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 GB/T 3077 12Cr2Ni4A
Match Breakdown
CHEMISTRY MATCH
65.9%
MECHANICAL MATCH
No shared data
OVERALL
65.9%
Specifications
Property IS 1570 (Part 7) 10Cr36Mo10H SAE J404 4130
Standard IS 1570 (Part 7):1992 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) <=0.15 0.28-0.33
Si (%) 0.25-1.0 0.15-0.35
Mn (%) 0.30-0.60 0.40-0.60
P (%) <=0.040 <=0.030
S (%) <=0.030 <=0.040
Cr (%) 8.00-10.00 0.80-1.10
Mo (%) 0.90-1.10 0.15-0.25
Al (metallic) (%) <=0.02 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 10Cr36Mo10H SAE J404 4130
Tensile Strength 410-560 MPa Not specified
Yield Strength >=135 MPa (0.2 % proof stress) Not specified
Elongation >=20% Not specified
Condition Pipes, A, thickness - (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
SAE J404 4130
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can IS 1570 (Part 7) 10Cr36Mo10H Be Substituted With SAE J404 4130?
IS 1570 (Part 7) 10Cr36Mo10H and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
SAE J404 4130
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 10Cr36Mo10H and SAE J404 4130?
IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for SAE J404 4130.
Can IS 1570 (Part 7) 10Cr36Mo10H be substituted with SAE J404 4130?
IS 1570 (Part 7) 10Cr36Mo10H and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.