IS 1570 (Part 7) 11Cr17Ni13W3TiH vs EN 10088-1 X12CrNiWTiB16-13

Close Alternative — 77.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) and EN 10088-1 X12CrNiWTiB16-13 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X12CrNiWTiB16-13 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 7) 11Cr17Ni13W3TiH vs EN 10088-1 X12CrNiWTiB16-13 is a 77.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.8%.

Frequently Compared With IS 1570 (Part 7) 11Cr17Ni13W3TiH:
EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 20Cr12MoNiVH GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13
Match Breakdown
CHEMISTRY MATCH
77.8%
MECHANICAL MATCH
No shared data
OVERALL
77.8%
Specifications
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 X12CrNiWTiB16-13
Standard IS 1570 (Part 7):1992 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.07-0.15
Si (%) <=1.00 <=0.50
Mn (%) <=1.00 <=1.50
P (%) <=0.045 <=0.035
S (%) <=0.030 <=0.015
Cr (%) 15.5-17.50 15.5-17.5
Ni (%) 12.00-14.50 12.5-14.5
W (%) 2.5-3.5 2.50-3.00
Ti (%) >=4xC, <=0.80 0.40-0.70
B (%) <=0.0006 0.0015-0.0060
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 X12CrNiWTiB16-13
Tensile Strength 600-800 MPa Not specified
Yield Strength >=390 MPa (0.2 % proof stress) Not specified
Elongation >=25% Not specified
Condition Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
EN 10088-1 X12CrNiWTiB16-13
Not documented
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH Be Substituted With EN 10088-1 X12CrNiWTiB16-13?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X12CrNiWTiB16-13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
EN 10088-1 X12CrNiWTiB16-13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X12CrNiWTiB16-13?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH be substituted with EN 10088-1 X12CrNiWTiB16-13?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X12CrNiWTiB16-13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.