IS 1570 (Part 7) 11Cr17Ni13W3TiH vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 11Cr17Ni13W3TiH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 7) 11Cr17Ni13W3TiH vs GOST 5632 08X18H10 is a 53.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) 11Cr17Ni13W3TiH:
EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
53.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10
Standard IS 1570 (Part 7):1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 ≤0.08
Si (%) <=1.00 ≤0.80
Mn (%) <=1.00 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 15.5-17.50 17.0–19.0
Ni (%) 12.00-14.50 9.0–11.0
W (%) 2.5-3.5 Not specified
Ti (%) >=4xC, <=0.80 Not specified
B (%) <=0.0006 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10
Tensile Strength 600-800 MPa ≥520 MPa
Yield Strength >=390 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=25% ≥40%
Condition Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 11Cr17Ni13W3TiH
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 11Cr17Ni13W3TiH and GOST 5632 08X18H10?
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for GOST 5632 08X18H10.
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH be substituted with GOST 5632 08X18H10?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.