IS 1570 (Part 7) 12Cr12MoVH vs GOST 5632 06Kh23N28

Minimal Match — 32.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 12Cr12MoVH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 7) 12Cr12MoVH vs GOST 5632 06Kh23N28 is a 49.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.7%.

Frequently Compared With IS 1570 (Part 7) 12Cr12MoVH:
IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4301 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 20Cr12MoNiVH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 ASTM A959 202 ASTM A959 201L
Match Breakdown
CHEMISTRY MATCH
49.1%
MECHANICAL MATCH
0%
OVERALL
32.7%
Specifications
Property IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28
Standard IS 1570 (Part 7):1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.08-0.16 ≤0.06
Si (%) <=0.60 ≤0.80
Mn (%) 0.40-1.00 ≤2.00
P (%) <=0.040 Not specified
S (%) <=0.035 Not specified
Cr (%) 11.5-13.00 22.0–25.0
Ni (%) <=1.0 26.0–29.0
Mo (%) 0.40-0.80 Not specified
V (%) 0.10-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28
Tensile Strength 770-930 MPa ≥510 MPa
Yield Strength >=585 MPa (0.2 % proof stress) ≥196 MPa
Elongation >=15% ≥35%
Condition Bars, forgings, Q+T, thickness up to 150 (first row of Table 3) Not specified
Max Service Temp Not specified 1050°C
Typical Applications
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can IS 1570 (Part 7) 12Cr12MoVH Be Substituted With GOST 5632 06Kh23N28?
IS 1570 (Part 7) 12Cr12MoVH and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 12Cr12MoVH
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 12Cr12MoVH and GOST 5632 06Kh23N28?
IS 1570 (Part 7) 12Cr12MoVH specifies P, S, Mo, V which are not specified for GOST 5632 06Kh23N28.
Can IS 1570 (Part 7) 12Cr12MoVH be substituted with GOST 5632 06Kh23N28?
IS 1570 (Part 7) 12Cr12MoVH and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.