IS 1570 (Part 7) 20Cr2MoVH vs ASTM A959 S41041

Related Material — 61.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 20Cr2MoVH (IS 1570 (Part 7):1992) and ASTM A959 S41041 (ASTM A959:2011) are both steel grades. IS 1570 (Part 7) 20Cr2MoVH is classified under Alloy Steel, while ASTM A959 S41041 is classified under Stainless Steel — a different category, which is worth noting alongside the chemistry match below. IS 1570 (Part 7) 20Cr2MoVH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while ASTM A959 S41041 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 1570 (Part 7) 20Cr2MoVH is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S41041 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 20Cr2MoVH vs ASTM A959 S41041 is a 61.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 61.4%.

Frequently Compared With IS 1570 (Part 7) 20Cr2MoVH:
GB/T 3077 12Cr2Ni4A IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr4Mo5H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 NF A35-565 100C6
Match Breakdown
CHEMISTRY MATCH
61.4%
MECHANICAL MATCH
No shared data
OVERALL
61.4%
Specifications
Property IS 1570 (Part 7) 20Cr2MoVH ASTM A959 S41041
Standard IS 1570 (Part 7):1992 ASTM A959:2011
Category Alloy Steel Stainless Steel
C (%) 0.20-0.30 0.13-0.18
Si (%) 0.20-0.50 <=0.50
Mn (%) 0.30-0.60 0.40-0.60
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Cr (%) 1.5-1.80 11.5-13.0
Ni (%) <=0.40 <=0.50
Mo (%) 0.60-0.80 <=0.20
V (%) 0.20-0.30 Not specified
Cu (%) <=0.30 Not specified
Al (%) Not specified <=0.05
Cb (%) Not specified 0.15-0.45
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 20Cr2MoVH ASTM A959 S41041
Tensile Strength 700-850 MPa Not specified
Yield Strength >=550 MPa (0.2 % proof stress) Not specified
Elongation >=17% Not specified
Condition Bars, forgings, Q+T, thickness - (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 20Cr2MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
ASTM A959 S41041
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 7) 20Cr2MoVH Be Substituted With ASTM A959 S41041?
IS 1570 (Part 7) 20Cr2MoVH and ASTM A959 S41041 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 20Cr2MoVH
0 active listings and RFQs →
ASTM A959 S41041
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 20Cr2MoVH and ASTM A959 S41041?
Different category: IS 1570 (Part 7) 20Cr2MoVH is Alloy Steel, ASTM A959 S41041 is Stainless Steel. IS 1570 (Part 7) 20Cr2MoVH specifies V, Cu which are not specified for ASTM A959 S41041. ASTM A959 S41041 specifies Al, Cb which are not specified for IS 1570 (Part 7) 20Cr2MoVH.
Can IS 1570 (Part 7) 20Cr2MoVH be substituted with ASTM A959 S41041?
IS 1570 (Part 7) 20Cr2MoVH and ASTM A959 S41041 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.