IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH vs GOST 5632 08X18H10

Minimal Match — 25.6% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH (IS 1570 (Part 7):1992) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH vs GOST 5632 08X18H10 is a 38.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 25.6%.

Frequently Compared With IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
38.4%
MECHANICAL MATCH
0%
OVERALL
25.6%
Specifications
Property IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH GOST 5632 08X18H10
Standard IS 1570 (Part 7):1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.03-0.08 ≤0.08
Si (%) <=1.00 ≤0.80
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 13.5-16.00 17.0–19.0
Ni (%) 24.00-27.00 9.0–11.0
Mo (%) 1.00-1.50 Not specified
V (%) 0.10-0.50 Not specified
Ti (%) 1.9-2.30 Not specified
Al (%) <=0.35 Not specified
B (%) 0.003-0.010 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH GOST 5632 08X18H10
Tensile Strength 900-1100 MPa ≥520 MPa
Yield Strength >=600 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=15% ≥40%
Condition Bars, forgings, pipes, plates, S+P, thickness over 5 to 250 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and GOST 5632 08X18H10?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH specifies Mo, V, Ti, Al which are not specified for GOST 5632 08X18H10.
Can IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH be substituted with GOST 5632 08X18H10?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.