IS 1570 (Part 7) 7Cr19Ni11TiH (IS 1570 (Part 7):1992) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 7Cr19Ni11TiH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. IS 1570 (Part 7) 7Cr19Ni11TiH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 7) 7Cr19Ni11TiH vs GOST 5632 06Kh23N28 is a 58.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) 7Cr19Ni11TiH:
EN 10088-1 1.4401 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
58.4%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 7) 7Cr19Ni11TiH GOST 5632 06Kh23N28
Standard IS 1570 (Part 7):1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 ≤0.06
Si (%) 0.20-0.80 ≤0.80
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 17.00-20.00 22.0–25.0
Ni (%) 9.00-13.00 26.0–29.0
Ti (%) <=0.60 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 7Cr19Ni11TiH GOST 5632 06Kh23N28
Tensile Strength 490-690 MPa ≥510 MPa
Yield Strength >=155 MPa (0.2 % proof stress) ≥196 MPa
Elongation >=30% ≥35%
Condition Pipes, bars, forgings, Q1, thickness - (first row of Table 3) Not specified
Max Service Temp Not specified 1050°C
Typical Applications
IS 1570 (Part 7) 7Cr19Ni11TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can IS 1570 (Part 7) 7Cr19Ni11TiH Be Substituted With GOST 5632 06Kh23N28?
IS 1570 (Part 7) 7Cr19Ni11TiH and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 7Cr19Ni11TiH
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
IS 1570 (Part 7) 7Cr19Ni11TiH
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 7Cr19Ni11TiH and GOST 5632 06Kh23N28?
IS 1570 (Part 7) 7Cr19Ni11TiH specifies P, S, Ti which are not specified for GOST 5632 06Kh23N28.
Can IS 1570 (Part 7) 7Cr19Ni11TiH be substituted with GOST 5632 06Kh23N28?
IS 1570 (Part 7) 7Cr19Ni11TiH and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.