IS 1570 (Part 7) 7Cr19Ni11TiH vs IS 1570 (Part 7) 12Cr12Ni2Mo

Minimal Match — 29.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 7Cr19Ni11TiH (IS 1570 (Part 7):1992) and IS 1570 (Part 7) 12Cr12Ni2Mo (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 7Cr19Ni11TiH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while IS 1570 (Part 7) 12Cr12Ni2Mo is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 7Cr19Ni11TiH is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr12Ni2Mo is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 7) 7Cr19Ni11TiH vs IS 1570 (Part 7) 12Cr12Ni2Mo is a 44.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 29.9%.

Frequently Compared With IS 1570 (Part 7) 7Cr19Ni11TiH:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
44.8%
MECHANICAL MATCH
0%
OVERALL
29.9%
Specifications
Property IS 1570 (Part 7) 7Cr19Ni11TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Standard IS 1570 (Part 7):1992 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 0.08-0.16
Si (%) 0.20-0.80 <=0.35
Mn (%) <=2.00 0.50-0.90
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 17.00-20.00 11.0-12.5
Ni (%) 9.00-13.00 2.0-3.0
Ti (%) <=0.60 Not specified
Mo (%) Not specified 1.5-2.00
V (%) Not specified 0.25-0.40
N (%) Not specified 0.02-0.04
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 7Cr19Ni11TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Tensile Strength 490-690 MPa 930-1130 MPa
Yield Strength >=155 MPa (0.2 % proof stress) >=785 MPa (0.2 % proof stress)
Elongation >=30% >=14%
Condition Pipes, bars, forgings, Q1, thickness - (first row of Table 3) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
IS 1570 (Part 7) 7Cr19Ni11TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 7) 12Cr12Ni2Mo
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 1570 (Part 7) 7Cr19Ni11TiH Be Substituted With IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 7Cr19Ni11TiH and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 7Cr19Ni11TiH
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12Ni2Mo
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 7Cr19Ni11TiH and IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 7Cr19Ni11TiH specifies Ti which is not specified for IS 1570 (Part 7) 12Cr12Ni2Mo. IS 1570 (Part 7) 12Cr12Ni2Mo specifies Mo, V, N which are not specified for IS 1570 (Part 7) 7Cr19Ni11TiH.
Can IS 1570 (Part 7) 7Cr19Ni11TiH be substituted with IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 7Cr19Ni11TiH and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.