IS 1570 (Part 7) Fe410H vs BS 970 (Part 1) 045M10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) Fe410H (IS 1570 (Part 7):1992) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 7) Fe410H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while BS 970 (Part 1) 045M10 is commonly used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties).. IS 1570 (Part 7) Fe410H is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 7) Fe410H vs BS 970 (Part 1) 045M10 is a 60.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) Fe410H:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 080A20 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
60.2%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 7) Fe410H BS 970 (Part 1) 045M10
Standard IS 1570 (Part 7):1992 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) <=0.20 0.07-0.13
Si (%) 0.10-0.35 Not specified
Mn (%) 0.50-1.30 0.30-0.60
P (%) <=0.03 <=0.050
S (%) <=0.03 <=0.050
Cr (%) <=0.25 Not specified
Ni (%) <=0.30 Not specified
Mo (%) <=0.10 Not specified
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) Fe410H BS 970 (Part 1) 045M10
Tensile Strength 410-520 MPa Not specified
Yield Strength >=225 MPa (0.2 % proof stress) Not specified
Elongation >=24% Not specified
Condition Plate, quadrangular seamless pipe, N, thickness over 3 to 16 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) Fe410H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
BS 970 (Part 1) 045M10
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
Key Differences
Can IS 1570 (Part 7) Fe410H Be Substituted With BS 970 (Part 1) 045M10?
IS 1570 (Part 7) Fe410H and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) Fe410H
0 active listings and RFQs →
BS 970 (Part 1) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) Fe410H and BS 970 (Part 1) 045M10?
IS 1570 (Part 7) Fe410H specifies Si, Cr, Ni, Mo which are not specified for BS 970 (Part 1) 045M10.
Can IS 1570 (Part 7) Fe410H be substituted with BS 970 (Part 1) 045M10?
IS 1570 (Part 7) Fe410H and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.