IS 1570 C30 (IS 1570:1961) and IS 1570 (Part 2/Sec 1) 30C8 (IS 1570 (Part 2/Sec 1):1979) are both steel grades. Both fall under the Carbon Steel category. IS 1570 C30 is typically used for axles, shafts, gears, connecting rods, machine parts, forgings, while IS 1570 (Part 2/Sec 1) 30C8 is commonly used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to is 1875, is 2004, is 3930, is 5517, is 6967). IS 1570 C30 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 2/Sec 1) 30C8 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 C30 vs IS 1570 (Part 2/Sec 1) 30C8 is a 93.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 95.4%.

Frequently Compared With IS 1570 C30:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
100%
OVERALL
95.4%
Specifications
Property IS 1570 C30 IS 1570 (Part 2/Sec 1) 30C8
Standard IS 1570:1961 IS 1570 (Part 2/Sec 1):1979
Category Carbon Steel Carbon Steel
C (%) 0.25-0.35 0.25-0.35
Mn (%) 0.60-0.90 0.60-0.90
Si (%) 0.15-0.35 Not specified
S (%) <=0.04 Not specified
P (%) <=0.04 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 C30 IS 1570 (Part 2/Sec 1) 30C8
Tensile Strength 500-600 MPa 500-600 MPa
Yield Strength >=275 MPa Not specified
Elongation >=21% >=21%
Hardness 143-187 HB Not specified
Typical Applications
IS 1570 C30
axles, shafts, gears, connecting rods, machine parts, forgings
IS 1570 (Part 2/Sec 1) 30C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517, IS 6967)
Key Differences
Can IS 1570 C30 Be Substituted With IS 1570 (Part 2/Sec 1) 30C8?
IS 1570 C30 and IS 1570 (Part 2/Sec 1) 30C8 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 2/Sec 1) 30C8 is often considered as a substitute for IS 1570 C30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 1570 C30
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5300–6200 mm (208.66–244.09 in)
IS 1570 (Part 2/Sec 1) 30C8
No active listings currently.
On M-EX Right Now
IS 1570 C30
2 active listings and RFQs →
IS 1570 (Part 2/Sec 1) 30C8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 C30 and IS 1570 (Part 2/Sec 1) 30C8?
IS 1570 C30 specifies Si, S, P which are not specified for IS 1570 (Part 2/Sec 1) 30C8.
Can IS 1570 C30 be substituted with IS 1570 (Part 2/Sec 1) 30C8?
IS 1570 C30 and IS 1570 (Part 2/Sec 1) 30C8 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 2/Sec 1) 30C8 is often considered as a substitute for IS 1570 C30 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.