Strong Match — 89% match
based on chemical composition and mechanical property overlap.
IS 4367 13Ni13Cr3 (IS 4367:1991) and BS 970 (Part 3) 655M13 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 4367 13Ni13Cr3 is typically used for gears, pinion gears, camshafts, transmission parts, aircraft components, heavy duty shafts, while BS 970 (Part 3) 655M13 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (table 15).
IS 4367 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 655M13 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, IS 4367 13Ni13Cr3 vs BS 970 (Part 3) 655M13 is a 89% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 89%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4367 13Ni13Cr3
BS 970 (Part 3) 655M13
Tensile Strength
850 MPa min
Not specified
Elongation
>=12%
Not specified
Izod Impact
48 J min
Not specified
Hardness (soft annealed)
<=229 HB
Not specified
Condition
Refined, quenched and stress relieved (core properties), ruling section up to 60 mm
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (Table 15)
Can IS 4367 13Ni13Cr3 Be Substituted With BS 970 (Part 3) 655M13?
IS 4367 13Ni13Cr3 and BS 970 (Part 3) 655M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 655M13 is often considered as a substitute for IS 4367 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 4367 13Ni13Cr3 and BS 970 (Part 3) 655M13?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4367 13Ni13Cr3 be substituted with BS 970 (Part 3) 655M13?
IS 4367 13Ni13Cr3 and BS 970 (Part 3) 655M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 655M13 is often considered as a substitute for IS 4367 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.