Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
IS 4367 13Ni13Cr3 (IS 4367:1991) and JIS G4102 SNC236 (JIS G 4102:1979) are both steel grades.
Both fall under the Alloy Steel category.
IS 4367 13Ni13Cr3 is typically used for gears, pinion gears, camshafts, transmission parts, aircraft components, heavy duty shafts, while JIS G4102 SNC236 is commonly used for used in gears, pinions, transmission shafts, axles, couplings, and automotive components..
IS 4367 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while JIS G4102 SNC236 is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, IS 4367 13Ni13Cr3 vs JIS G4102 SNC236 is a 89.5% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4367 13Ni13Cr3
JIS G4102 SNC236
Tensile Strength
850 MPa min
850-1050 MPa
Elongation
>=12%
12% min
Izod Impact
48 J min
Not specified
Hardness (soft annealed)
<=229 HB
Not specified
Condition
Refined, quenched and stress relieved (core properties), ruling section up to 60 mm
Used in gears, pinions, transmission shafts, axles, couplings, and automotive components.
Can IS 4367 13Ni13Cr3 Be Substituted With JIS G4102 SNC236?
IS 4367 13Ni13Cr3 and JIS G4102 SNC236 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 4367 13Ni13Cr3 and JIS G4102 SNC236?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4367 13Ni13Cr3 be substituted with JIS G4102 SNC236?
IS 4367 13Ni13Cr3 and JIS G4102 SNC236 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.