Minimal Match — 41.5% match
based on chemical composition and mechanical property overlap.
IS 4367 16Ni8Cr6Mo2 (IS 4367:1991) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 4367 16Ni8Cr6Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 4367 16Ni8Cr6Mo2 vs IS 4367 07Cr4Mo6 is a 62.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 41.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4367 16Ni8Cr6Mo2
IS 4367 07Cr4Mo6
Tensile Strength
1350 MPa min
380-550 MPa
Elongation
>=9%
>=19%
Izod Impact
35 J min
60 J min
Hardness (soft annealed)
<=229 HB
<=170 HB
Condition
Refined, quenched and stress relieved (core properties), ruling section up to 30 mm
Normalised and tempered, ruling section up to 40 mm
Can IS 4367 16Ni8Cr6Mo2 Be Substituted With IS 4367 07Cr4Mo6?
IS 4367 16Ni8Cr6Mo2 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 4367 16Ni8Cr6Mo2 and IS 4367 07Cr4Mo6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4367 16Ni8Cr6Mo2 be substituted with IS 4367 07Cr4Mo6?
IS 4367 16Ni8Cr6Mo2 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.