IS 4367 20Mn5Cr5 vs IS 11169 (Part 1) 20MnCr5

Strong Match — 86.6% match based on chemical composition and mechanical property overlap.

IS 4367 20Mn5Cr5 (IS 4367:1991) and IS 11169 (Part 1) 20MnCr5 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. IS 4367 20Mn5Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 20MnCr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 20Mn5Cr5 vs IS 11169 (Part 1) 20MnCr5 is a 96.6% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a strong match overall at 86.6%.

Frequently Compared With IS 4367 20Mn5Cr5:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6
Match Breakdown
CHEMISTRY MATCH
96.6%
MECHANICAL MATCH
66.7%
OVERALL
86.6%
Specifications
Property IS 4367 20Mn5Cr5 IS 11169 (Part 1) 20MnCr5
Standard IS 4367:1991 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.18-0.22 0.17-0.22
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 1.00-1.40 1.00-1.40
Cr (%) 1.00-1.30 1.00-1.30
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 20Mn5Cr5 IS 11169 (Part 1) 20MnCr5
Tensile Strength 1000 MPa min Not specified
Elongation >=8% Not specified
Izod Impact 38 J min Not specified
Hardness (soft annealed) <=217 HB Not specified
Condition Refined, quenched and stress relieved (core properties), ruling section up to 30 mm Not specified
Core Tensile Strength Not specified >=1000 MPa (30 mm)
Core Elongation Not specified >=8% (30 mm)
Hardness, annealed Not specified <=170 HB
Typical Applications
IS 4367 20Mn5Cr5
Not documented
IS 11169 (Part 1) 20MnCr5
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can IS 4367 20Mn5Cr5 Be Substituted With IS 11169 (Part 1) 20MnCr5?
IS 4367 20Mn5Cr5 and IS 11169 (Part 1) 20MnCr5 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 20MnCr5 is often considered as a substitute for IS 4367 20Mn5Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 4367 20Mn5Cr5
0 active listings and RFQs →
IS 11169 (Part 1) 20MnCr5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 20Mn5Cr5 and IS 11169 (Part 1) 20MnCr5?
IS 4367 20Mn5Cr5 specifies S, P which are not specified for IS 11169 (Part 1) 20MnCr5.
Can IS 4367 20Mn5Cr5 be substituted with IS 11169 (Part 1) 20MnCr5?
IS 4367 20Mn5Cr5 and IS 11169 (Part 1) 20MnCr5 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 20MnCr5 is often considered as a substitute for IS 4367 20Mn5Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.