IS 4367 50Cr4V2 vs BS 970 (Part 1) 530A40

Close Alternative — 77.7% match based on chemical composition and mechanical property overlap.

IS 4367 50Cr4V2 (IS 4367:1991) and BS 970 (Part 1) 530A40 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 4367 50Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 530A40 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 4367 50Cr4V2 vs BS 970 (Part 1) 530A40 is a 77.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.7%.

Frequently Compared With IS 4367 50Cr4V2:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 NF A35-565 100C6
Match Breakdown
CHEMISTRY MATCH
77.7%
MECHANICAL MATCH
No shared data
OVERALL
77.7%
Specifications
Property IS 4367 50Cr4V2 BS 970 (Part 1) 530A40
Standard IS 4367:1991 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.45-0.55 0.38-0.43
Si (%) 0.10-0.35 Not specified
Mn (%) 0.50-0.80 0.60-0.80
Cr (%) 0.90-1.20 0.90-1.20
V (%) 0.15-0.30 Not specified
S (%) <=0.035 <=0.040
P (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 50Cr4V2 BS 970 (Part 1) 530A40
Tensile Strength 900-1100 MPa Not specified
Yield Strength 700 MPa min Not specified
Elongation >=12% Not specified
Izod Impact 45 J min Not specified
Hardness 266-325 HB Not specified
Hardness (soft annealed) <=240 HB Not specified
Condition Hardened and tempered, ruling section up to 100 mm Not specified
Typical Applications
IS 4367 50Cr4V2
Not documented
BS 970 (Part 1) 530A40
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can IS 4367 50Cr4V2 Be Substituted With BS 970 (Part 1) 530A40?
IS 4367 50Cr4V2 and BS 970 (Part 1) 530A40 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 4367 50Cr4V2
0 active listings and RFQs →
BS 970 (Part 1) 530A40
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 50Cr4V2 and BS 970 (Part 1) 530A40?
IS 4367 50Cr4V2 specifies Si, V which are not specified for BS 970 (Part 1) 530A40.
Can IS 4367 50Cr4V2 be substituted with BS 970 (Part 1) 530A40?
IS 4367 50Cr4V2 and BS 970 (Part 1) 530A40 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.