IS 4432 13Ni13Cr3 vs BS 970 (Part 1) 655H13

Strong Match — 85.1% match based on chemical composition and mechanical property overlap.

IS 4432 13Ni13Cr3 (IS 4432:1988) and BS 970 (Part 1) 655H13 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 4432 13Ni13Cr3 is typically used for forgings and fabrication of case-hardened machine or automobile parts, while BS 970 (Part 1) 655H13 is commonly used for case hardening steel supplied to specified hardenability limits (end quench test, table 10).. IS 4432 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 655H13 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 4432 13Ni13Cr3 vs BS 970 (Part 1) 655H13 is a 85.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.1%.

Frequently Compared With IS 4432 13Ni13Cr3:
IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
85.1%
MECHANICAL MATCH
No shared data
OVERALL
85.1%
Specifications
Property IS 4432 13Ni13Cr3 BS 970 (Part 1) 655H13
Standard IS 4432:1988 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.10-0.15 0.10-0.16
Si (%) 0.15-0.35 Not specified
Mn (%) 0.40-0.70 0.35-0.60
Ni (%) 3.00-3.50 3.00-3.75
Cr (%) 0.60-1.00 0.70-1.00
S (%) <=0.035 <=0.040
P (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4432 13Ni13Cr3 BS 970 (Part 1) 655H13
Core Tensile Strength 1000-1300 MPa (16 mm) / 900-1250 MPa (30 mm) / 850-1200 MPa (63 mm) Not specified
Core Yield Strength >=720 MPa (16 mm) / >=650 MPa (30 mm) / >=600 MPa (63 mm) Not specified
Core Elongation >=8% (16 mm) / >=9% (30 mm) / >=10% (63 mm) Not specified
Core Reduction of Area >=35% (16 mm) / >=35% (30 mm) / >=40% (63 mm) Not specified
Hardness, annealed (A) <=217 HB Not specified
Typical Applications
IS 4432 13Ni13Cr3
Forgings and fabrication of case-hardened machine or automobile parts
BS 970 (Part 1) 655H13
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
Key Differences
Can IS 4432 13Ni13Cr3 Be Substituted With BS 970 (Part 1) 655H13?
IS 4432 13Ni13Cr3 and BS 970 (Part 1) 655H13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 655H13 is often considered as a substitute for IS 4432 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 4432 13Ni13Cr3
0 active listings and RFQs →
BS 970 (Part 1) 655H13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4432 13Ni13Cr3 and BS 970 (Part 1) 655H13?
IS 4432 13Ni13Cr3 specifies Si which is not specified for BS 970 (Part 1) 655H13.
Can IS 4432 13Ni13Cr3 be substituted with BS 970 (Part 1) 655H13?
IS 4432 13Ni13Cr3 and BS 970 (Part 1) 655H13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 655H13 is often considered as a substitute for IS 4432 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.