IS 5517 40C10S18 vs BS 970 (Part 3) 216M36

Strong Match — 87.7% match based on chemical composition and mechanical property overlap.

IS 5517 40C10S18 (IS 5517:1993) and BS 970 (Part 3) 216M36 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Free Machining Steel category. IS 5517 40C10S18 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 216M36 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 5517 40C10S18 vs BS 970 (Part 3) 216M36 is a 87.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.7%.

Frequently Compared With IS 5517 40C10S18:
IS 1570 (Part 3) 10C8S10 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1132 SAE J403 1132 SAE J403 1117 SAE J403 1117 SAE J403 1118 SAE J403 1118 SAE J403 1126 SAE J403 1126
Match Breakdown
CHEMISTRY MATCH
87.7%
MECHANICAL MATCH
No shared data
OVERALL
87.7%
Specifications
Property IS 5517 40C10S18 BS 970 (Part 3) 216M36
Standard IS 5517:1993 BS 970 (Part 3):1991
Category Free Machining Steel Free Machining Steel
C (%) 0.35-0.45 0.32-0.40
Si (%) <=0.25 <=0.25
Mn (%) 0.80-1.20 1.30-1.70
S (%) 0.14-0.22 0.12-0.20
P (%) <=0.060 <=0.06
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 40C10S18 BS 970 (Part 3) 216M36
Tensile Strength 600-750 MPa Not specified
Yield Strength (0.2% proof) 380 MPa min Not specified
Elongation >=18% Not specified
Izod Impact 41 J min Not specified
Hardness (annealed) <=200 HB Not specified
Condition Hardened and tempered, ruling section up to 60 mm Not specified
Typical Applications
IS 5517 40C10S18
Not documented
BS 970 (Part 3) 216M36
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; free-cutting steel (Table 12)
Can IS 5517 40C10S18 Be Substituted With BS 970 (Part 3) 216M36?
IS 5517 40C10S18 and BS 970 (Part 3) 216M36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 216M36 is often considered as a substitute for IS 5517 40C10S18 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 5517 40C10S18
0 active listings and RFQs →
BS 970 (Part 3) 216M36
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 40C10S18 and BS 970 (Part 3) 216M36?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5517 40C10S18 be substituted with BS 970 (Part 3) 216M36?
IS 5517 40C10S18 and BS 970 (Part 3) 216M36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 216M36 is often considered as a substitute for IS 5517 40C10S18 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.