IS 5522 X07Cr18Ni9 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 5522 X07Cr18Ni9 (IS 5522:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 5522 X07Cr18Ni9 is typically used for utensils, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. IS 5522 X07Cr18Ni9 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 5522 X07Cr18Ni9 vs GOST 5632 08X18H10 is a 74.8% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 5522 X07Cr18Ni9:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
74.8%
MECHANICAL MATCH
66.7%
OVERALL
35%
Specifications
Property IS 5522 X07Cr18Ni9 GOST 5632 08X18H10
Standard IS 5522:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 ≤0.08
Si (%) <=0.75 ≤0.80
Mn (%) <=2.00 ≤2.00
Ni (%) 8.0-10.0 9.0–11.0
Cr (%) 17.0-19.0 17.0–19.0
S (%) <=0.030 ≤0.020
P (%) <=0.045 ≤0.035
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5522 X07Cr18Ni9 GOST 5632 08X18H10
Tensile Strength >=515 MPa ≥520 MPa
Yield Strength >=205 MPa ≥205 MPa
Elongation >=40% ≥40%
Hardness <=201 HB Not specified
Condition Annealed/softened Not specified
Typical Applications
IS 5522 X07Cr18Ni9
Utensils
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 5522 X07Cr18Ni9 Be Substituted With GOST 5632 08X18H10?
IS 5522 X07Cr18Ni9 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 5522 X07Cr18Ni9
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 5522 X07Cr18Ni9
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5522 X07Cr18Ni9 and GOST 5632 08X18H10?
IS 5522 X07Cr18Ni9 specifies N which is not specified for GOST 5632 08X18H10.
Can IS 5522 X07Cr18Ni9 be substituted with GOST 5632 08X18H10?
IS 5522 X07Cr18Ni9 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.