IS 6603 X01Cr24Ni22Mo4CuNW vs EN 10088-1 X1CrNiMoCuNW24-22-6

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 6603 X01Cr24Ni22Mo4CuNW (IS 6603:2024) and EN 10088-1 X1CrNiMoCuNW24-22-6 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X01Cr24Ni22Mo4CuNW is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X1CrNiMoCuNW24-22-6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X01Cr24Ni22Mo4CuNW vs EN 10088-1 X1CrNiMoCuNW24-22-6 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 6603 X01Cr24Ni22Mo4CuNW:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 6603 X01Cr24Ni22Mo4CuNW EN 10088-1 X1CrNiMoCuNW24-22-6
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.70
Mn (%) 2.0-4.0 2.00-4.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.010
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 5.5-6.5 5.5-6.5
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.35-0.50 0.35-0.50
Cu (%) 1.00-2.00 1.00-2.00
W (%) 1.50-2.50 1.50-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X01Cr24Ni22Mo4CuNW EN 10088-1 X1CrNiMoCuNW24-22-6
Tensile Strength 800-1000 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=50% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 60 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X01Cr24Ni22Mo4CuNW
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X1CrNiMoCuNW24-22-6
Not documented
Can IS 6603 X01Cr24Ni22Mo4CuNW Be Substituted With EN 10088-1 X1CrNiMoCuNW24-22-6?
IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 X1CrNiMoCuNW24-22-6 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X1CrNiMoCuNW24-22-6 is often considered as a substitute for IS 6603 X01Cr24Ni22Mo4CuNW in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X01Cr24Ni22Mo4CuNW
0 active listings and RFQs →
EN 10088-1 X1CrNiMoCuNW24-22-6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 X1CrNiMoCuNW24-22-6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X01Cr24Ni22Mo4CuNW be substituted with EN 10088-1 X1CrNiMoCuNW24-22-6?
IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 X1CrNiMoCuNW24-22-6 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X1CrNiMoCuNW24-22-6 is often considered as a substitute for IS 6603 X01Cr24Ni22Mo4CuNW in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.