IS 6603 X01Cr24Ni22Mo7CuN vs EN 10088-1 X1CrNiMoCuNW24-22-6

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 6603 X01Cr24Ni22Mo7CuN (IS 6603:2024) and EN 10088-1 X1CrNiMoCuNW24-22-6 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X01Cr24Ni22Mo7CuN is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X1CrNiMoCuNW24-22-6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X01Cr24Ni22Mo7CuN vs EN 10088-1 X1CrNiMoCuNW24-22-6 is a 76.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 6603 X01Cr24Ni22Mo7CuN:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
76.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 6603 X01Cr24Ni22Mo7CuN EN 10088-1 X1CrNiMoCuNW24-22-6
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.50 <=0.70
Mn (%) 2.0-4.0 2.00-4.0
P (%) <=0.030 <=0.030
S (%) <=0.005 <=0.010
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 7.0-8.0 5.5-6.5
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.45-0.55 0.35-0.50
Cu (%) 0.30-0.60 1.00-2.00
W (%) Not specified 1.50-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X01Cr24Ni22Mo7CuN EN 10088-1 X1CrNiMoCuNW24-22-6
Tensile Strength 750-1050 MPa Not specified
Yield Strength >=430 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X01Cr24Ni22Mo7CuN
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X1CrNiMoCuNW24-22-6
Not documented
Key Differences
Can IS 6603 X01Cr24Ni22Mo7CuN Be Substituted With EN 10088-1 X1CrNiMoCuNW24-22-6?
IS 6603 X01Cr24Ni22Mo7CuN and EN 10088-1 X1CrNiMoCuNW24-22-6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X01Cr24Ni22Mo7CuN
0 active listings and RFQs →
EN 10088-1 X1CrNiMoCuNW24-22-6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X01Cr24Ni22Mo7CuN and EN 10088-1 X1CrNiMoCuNW24-22-6?
EN 10088-1 X1CrNiMoCuNW24-22-6 specifies W which is not specified for IS 6603 X01Cr24Ni22Mo7CuN.
Can IS 6603 X01Cr24Ni22Mo7CuN be substituted with EN 10088-1 X1CrNiMoCuNW24-22-6?
IS 6603 X01Cr24Ni22Mo7CuN and EN 10088-1 X1CrNiMoCuNW24-22-6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.