IS 6603 X01Ni25Cr20Mo5Cu vs EN 10088-2 X1NiCrMoCu25-20-5
Close Alternative — 84.8% match
based on chemical composition and mechanical property overlap.
IS 6603 X01Ni25Cr20Mo5Cu (IS 6603:2024) and EN 10088-2 X1NiCrMoCu25-20-5 (EN 10088-2:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X01Ni25Cr20Mo5Cu is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-2 X1NiCrMoCu25-20-5 is commonly used for general purposes, hot or cold rolled sheet/plate and strip.
IS 6603 X01Ni25Cr20Mo5Cu is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-2 X1NiCrMoCu25-20-5 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6603 X01Ni25Cr20Mo5Cu vs EN 10088-2 X1NiCrMoCu25-20-5 is a 93.9% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a close alternative overall at 84.8%.
Frequently Compared With IS 6603 X01Ni25Cr20Mo5Cu:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X01Ni25Cr20Mo5Cu
EN 10088-2 X1NiCrMoCu25-20-5
Tensile Strength
530-730 MPa
530-730 MPa
Yield Strength
>=220 MPa
>=240 MPa
Elongation
>=35%
>=35%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
IS 6603 X01Ni25Cr20Mo5Cu
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-2 X1NiCrMoCu25-20-5
General purposes, hot or cold rolled sheet/plate and strip
Can IS 6603 X01Ni25Cr20Mo5Cu Be Substituted With EN 10088-2 X1NiCrMoCu25-20-5?
IS 6603 X01Ni25Cr20Mo5Cu and EN 10088-2 X1NiCrMoCu25-20-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 6603 X01Ni25Cr20Mo5Cu and EN 10088-2 X1NiCrMoCu25-20-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X01Ni25Cr20Mo5Cu be substituted with EN 10088-2 X1NiCrMoCu25-20-5?
IS 6603 X01Ni25Cr20Mo5Cu and EN 10088-2 X1NiCrMoCu25-20-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.