IS 6603 X02Cr18Mo2TiS vs EN 10088-1 X2CrMoTiS18-2

Strong Match — 91.7% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr18Mo2TiS (IS 6603:2024) and EN 10088-1 X2CrMoTiS18-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr18Mo2TiS is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrMoTiS18-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr18Mo2TiS vs EN 10088-1 X2CrMoTiS18-2 is a 91.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.7%.

Frequently Compared With IS 6603 X02Cr18Mo2TiS:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
91.7%
MECHANICAL MATCH
No shared data
OVERALL
91.7%
Specifications
Property IS 6603 X02Cr18Mo2TiS EN 10088-1 X2CrMoTiS18-2
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=0.50 <=0.50
P (%) <=0.040 <=0.040
S (%) >=0.15 0.15-0.35
Cr (%) 17.5-19.0 17.5-19.0
Mo (%) 2.00-2.50 2.00-2.50
Ti (%) 0.30-0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr18Mo2TiS EN 10088-1 X2CrMoTiS18-2
Tensile Strength >=430 MPa Not specified
Yield Strength >=280 MPa Not specified
Elongation >=15% Not specified
Hardness <=200 HB Not specified
Condition Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Tensile Strength is a minimum as printed Not specified
Typical Applications
IS 6603 X02Cr18Mo2TiS
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X2CrMoTiS18-2
Not documented
Key Differences
Can IS 6603 X02Cr18Mo2TiS Be Substituted With EN 10088-1 X2CrMoTiS18-2?
IS 6603 X02Cr18Mo2TiS and EN 10088-1 X2CrMoTiS18-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrMoTiS18-2 is often considered as a substitute for IS 6603 X02Cr18Mo2TiS in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X02Cr18Mo2TiS
0 active listings and RFQs →
EN 10088-1 X2CrMoTiS18-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr18Mo2TiS and EN 10088-1 X2CrMoTiS18-2?
IS 6603 X02Cr18Mo2TiS specifies Ti which is not specified for EN 10088-1 X2CrMoTiS18-2.
Can IS 6603 X02Cr18Mo2TiS be substituted with EN 10088-1 X2CrMoTiS18-2?
IS 6603 X02Cr18Mo2TiS and EN 10088-1 X2CrMoTiS18-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrMoTiS18-2 is often considered as a substitute for IS 6603 X02Cr18Mo2TiS in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.