IS 6603 X02Cr18Ni9N vs ASTM A959 .-

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr18Ni9N (IS 6603:2024) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr18Ni9N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 6603 X02Cr18Ni9N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, IS 6603 X02Cr18Ni9N vs ASTM A959 .- is a 74.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 6603 X02Cr18Ni9N:
GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
74.1%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 6603 X02Cr18Ni9N ASTM A959 .-
Standard IS 6603:2024 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 17.5-19.5 18.0-20.0
Ni (%) 8.0-10.0 <=0.50
N (%) 0.12-0.22 <=0.030
Cb (%) Not specified 0.10-0.60
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr18Ni9N ASTM A959 .-
Tensile Strength 550-750 MPa Not specified
Yield Strength >=270 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X02Cr18Ni9N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 6603 X02Cr18Ni9N Be Substituted With ASTM A959 .-?
IS 6603 X02Cr18Ni9N and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X02Cr18Ni9N
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr18Ni9N and ASTM A959 .-?
ASTM A959 .- specifies Cb, Ti which are not specified for IS 6603 X02Cr18Ni9N.
Can IS 6603 X02Cr18Ni9N be substituted with ASTM A959 .-?
IS 6603 X02Cr18Ni9N and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.