Strong Match — 87.8% match
based on chemical composition and mechanical property overlap.
IS 6603 X02Cr22Ni5Mo3N (IS 6603:2024) and ASTM A959 2205 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X02Cr22Ni5Mo3N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 2205 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
IS 6603 X02Cr22Ni5Mo3N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 2205 is defined under ASTM International, originating from United States.
As per chemical composition, IS 6603 X02Cr22Ni5Mo3N vs ASTM A959 2205 is a 87.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 87.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X02Cr22Ni5Mo3N
ASTM A959 2205
Tensile Strength
>=650 MPa
Not specified
Yield Strength
>=450 MPa
Not specified
Elongation
>=25%
Not specified
Hardness
<=290 HB
Not specified
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Not specified
Typical Applications
IS 6603 X02Cr22Ni5Mo3N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 2205
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 6603 X02Cr22Ni5Mo3N Be Substituted With ASTM A959 2205?
IS 6603 X02Cr22Ni5Mo3N and ASTM A959 2205 overlap closely enough on chemistry and mechanical properties that ASTM A959 2205 is often considered as a substitute for IS 6603 X02Cr22Ni5Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6603 X02Cr22Ni5Mo3N and ASTM A959 2205?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X02Cr22Ni5Mo3N be substituted with ASTM A959 2205?
IS 6603 X02Cr22Ni5Mo3N and ASTM A959 2205 overlap closely enough on chemistry and mechanical properties that ASTM A959 2205 is often considered as a substitute for IS 6603 X02Cr22Ni5Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.