IS 6603:2024 X02Cr22Ni5Mo3N Steel: Specifications & Listings

IS 6603:2024 X02Cr22Ni5Mo3N: X02Cr22Ni5Mo3N: austenitic-ferritic (duplex) corrosion resisting stainless steel, numerical symbol 2205. Specified in IS 6603:2024.

Category: Stainless Steel
Grade Details
GradeIS 6603:2024 X02Cr22Ni5Mo3N
Standard IS 6603:2024
ApplicationsGeneral purposes, semi-finished products, bars, wire rods and bright bars
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S31803 ASTM A959:2011 USA No activity yet
ASTM A959 2205 ASTM A959:2011 USA No activity yet
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2023 Strong Match
ASTM A959 S31803 ASTM A959:2011 Strong Match
ASTM A959 2205 ASTM A959:2011 Strong Match
ASTM A276/A276M S32205 ASTM A276/A276M:2017 Close Alternative
EN 10088-3 X2CrNiMoN22-5-3 EN 10088-3:2014 Close Alternative
ASTM A240/A240M S31803 ASTM A240/A240M:2025 Close Alternative
ASTM A276/A276M S31803 ASTM A276/A276M:2017 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni N
<=0.030 <=1.00 <=2.00 <=0.035 <=0.015 21.0-23.0 2.5-3.5 4.5-6.5 0.10-0.22
Mechanical Properties
Tensile Strength >=650 MPa
Yield Strength >=450 MPa
Elongation >=25%
Hardness <=290 HB
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only

More data from IS 6603:2024

From the standard
Mechanical properties by thickness or diameter 1 size range
Thickness or diameter (mm)Hardness HB (guidance)Rp0.2 min (MPa)Rm min (MPa)A min (%)KV2 min (J)
up to 16029045065025100
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: IS 6603:2024, Table 6
Bright bars, solution annealed 5 rows
Thickness or diameter (mm)Rp0.2 min (MPa)Rm (MPa)A5 min (%)KV2 min (J)
up to 10650850 to 115012-
over 10 to 16650850 to 110012-
over 16 to 40450650 to 100015100
over 40 to 63450650 to 100015100
over 63 to 160450650 to 88025100
Bright bars, conditions 2H, 2B, 2G or 2P; A5 valid for 5 mm and above.
Source: IS 6603:2024, Table 16
Proof strength at elevated temperature 4 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100360
150335
200315
250300
Minimum values, solution annealed (+AT); for guidance only.
Source: IS 6603:2024, Table 11
Hot forming and solution annealing guideline temperatures
Hot forming temperature
1200 to 950 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1020 to 1100 deg C
Cooling after solution annealing
water, air
Informative guideline (Annex A).
Source: IS 6603:2024, Table 21

Active IS 6603:2024 X02Cr22Ni5Mo3N Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 6603:2024 X02Cr22Ni5Mo3N listings at this time.

Register for Alerts

Buyer RFQs for IS 6603:2024 X02Cr22Ni5Mo3N

+ Post an RFQ for this grade

No open buyer requirements for IS 6603:2024 X02Cr22Ni5Mo3N at this time.

Register for Alerts