IS 6603 X02Cr25Ni18Mn6Mo4N vs EN 10088-2 X2CrNiMnMoN25-18-6-5

Strong Match — 85.5% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr25Ni18Mn6Mo4N (IS 6603:2024) and EN 10088-2 X2CrNiMnMoN25-18-6-5 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr25Ni18Mn6Mo4N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-2 X2CrNiMnMoN25-18-6-5 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. IS 6603 X02Cr25Ni18Mn6Mo4N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-2 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr25Ni18Mn6Mo4N vs EN 10088-2 X2CrNiMnMoN25-18-6-5 is a 99.1% match. As per mechanical properties, the match is 58.3%. Combined, this makes them a strong match overall at 85.5%.

Frequently Compared With IS 6603 X02Cr25Ni18Mn6Mo4N:
EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
99.1%
MECHANICAL MATCH
58.3%
OVERALL
85.5%
Specifications
Property IS 6603 X02Cr25Ni18Mn6Mo4N EN 10088-2 X2CrNiMnMoN25-18-6-5
Standard IS 6603:2024 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-7.0 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 4.0-5.0 4.0-5.0
Ni (%) 16.0-19.0 16.0-19.0
N (%) 0.30-0.60 0.30-0.60
Nb (%) <=0.15 <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr25Ni18Mn6Mo4N EN 10088-2 X2CrNiMnMoN25-18-6-5
Tensile Strength 800-1000 MPa 800-950 MPa
Yield Strength >=420 MPa >=420 MPa
Elongation >=35% >=30%
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Solution annealed (+AT), cold rolled strip, up to 6 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
IS 6603 X02Cr25Ni18Mn6Mo4N
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-2 X2CrNiMnMoN25-18-6-5
General purposes, hot or cold rolled sheet/plate and strip
Can IS 6603 X02Cr25Ni18Mn6Mo4N Be Substituted With EN 10088-2 X2CrNiMnMoN25-18-6-5?
IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-2 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for IS 6603 X02Cr25Ni18Mn6Mo4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X02Cr25Ni18Mn6Mo4N
0 active listings and RFQs →
EN 10088-2 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-2 X2CrNiMnMoN25-18-6-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X02Cr25Ni18Mn6Mo4N be substituted with EN 10088-2 X2CrNiMnMoN25-18-6-5?
IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-2 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for IS 6603 X02Cr25Ni18Mn6Mo4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.