IS 6603 X02Cr25Ni7Mo4N vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr25Ni7Mo4N (IS 6603:2024) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr25Ni7Mo4N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. IS 6603 X02Cr25Ni7Mo4N is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 6603 X02Cr25Ni7Mo4N vs GB/T 3280 06Cr19Ni10 is a 62.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6603 X02Cr25Ni7Mo4N:
IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4845 ASTM A959 2507 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
62.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6603 X02Cr25Ni7Mo4N GB/T 3280 06Cr19Ni10
Standard IS 6603:2024 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) <=1.00 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.035 0.045 max
S (%) <=0.015 0.030 max
Cr (%) 24.0-26.0 18.00-20.00
Mo (%) 3.0-4.5 Not specified
Ni (%) 6.0-8.0 8.00-11.00
N (%) 0.24-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr25Ni7Mo4N GB/T 3280 06Cr19Ni10
Tensile Strength >=730 MPa 520-720 MPa
Yield Strength >=530 MPa 205-310 MPa
Elongation >=25% 40-60%
Hardness <=290 HB 187 HB max
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only Not specified
Typical Applications
IS 6603 X02Cr25Ni7Mo4N
General purposes, semi-finished products, bars, wire rods and bright bars
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can IS 6603 X02Cr25Ni7Mo4N Be Substituted With GB/T 3280 06Cr19Ni10?
IS 6603 X02Cr25Ni7Mo4N and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6603 X02Cr25Ni7Mo4N
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
IS 6603 X02Cr25Ni7Mo4N
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr25Ni7Mo4N and GB/T 3280 06Cr19Ni10?
IS 6603 X02Cr25Ni7Mo4N specifies Mo, N which are not specified for GB/T 3280 06Cr19Ni10.
Can IS 6603 X02Cr25Ni7Mo4N be substituted with GB/T 3280 06Cr19Ni10?
IS 6603 X02Cr25Ni7Mo4N and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.