Strong Match — 89.9% match
based on chemical composition and mechanical property overlap.
IS 6603 X02Cr25Ni7Mo4N (IS 6603:2024) and ASTM A959 2507 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X02Cr25Ni7Mo4N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 2507 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
IS 6603 X02Cr25Ni7Mo4N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 2507 is defined under ASTM International, originating from United States.
As per chemical composition, IS 6603 X02Cr25Ni7Mo4N vs ASTM A959 2507 is a 89.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 89.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X02Cr25Ni7Mo4N
ASTM A959 2507
Tensile Strength
>=730 MPa
Not specified
Yield Strength
>=530 MPa
Not specified
Elongation
>=25%
Not specified
Hardness
<=290 HB
Not specified
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Not specified
Typical Applications
IS 6603 X02Cr25Ni7Mo4N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 2507
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
ASTM A959 2507 specifies Cu which is not specified for IS 6603 X02Cr25Ni7Mo4N.
Can IS 6603 X02Cr25Ni7Mo4N Be Substituted With ASTM A959 2507?
IS 6603 X02Cr25Ni7Mo4N and ASTM A959 2507 overlap closely enough on chemistry and mechanical properties that ASTM A959 2507 is often considered as a substitute for IS 6603 X02Cr25Ni7Mo4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6603 X02Cr25Ni7Mo4N and ASTM A959 2507?
ASTM A959 2507 specifies Cu which is not specified for IS 6603 X02Cr25Ni7Mo4N.
Can IS 6603 X02Cr25Ni7Mo4N be substituted with ASTM A959 2507?
IS 6603 X02Cr25Ni7Mo4N and ASTM A959 2507 overlap closely enough on chemistry and mechanical properties that ASTM A959 2507 is often considered as a substitute for IS 6603 X02Cr25Ni7Mo4N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.