IS 6603 X04Cr17Ni12Mo2Ti vs EN 10088-1 1.4006

Minimal Match — 32.9% match based on chemical composition and mechanical property overlap.

IS 6603 X04Cr17Ni12Mo2Ti (IS 6603:2024) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X04Cr17Ni12Mo2Ti is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 6603 X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X04Cr17Ni12Mo2Ti vs EN 10088-1 1.4006 is a 49.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.9%.

Frequently Compared With IS 6603 X04Cr17Ni12Mo2Ti:
EN 10088-1 1.4401 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
49.4%
MECHANICAL MATCH
0%
OVERALL
32.9%
Specifications
Property IS 6603 X04Cr17Ni12Mo2Ti EN 10088-1 1.4006
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 16.0-18.0 11.5–13.5
Mo (%) 2.00-2.50 Not specified
Ni (%) 10.0-13.5 ≤0.75
Ti (%) <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X04Cr17Ni12Mo2Ti EN 10088-1 1.4006
Tensile Strength 520-720 MPa ≥540 MPa (annealed)
Yield Strength >=205 MPa Not specified
Elongation >=40% ≥18%
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 6603 X04Cr17Ni12Mo2Ti
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 6603 X04Cr17Ni12Mo2Ti Be Substituted With EN 10088-1 1.4006?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6603 X04Cr17Ni12Mo2Ti
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 6603 X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4006?
IS 6603 X04Cr17Ni12Mo2Ti specifies P, S, Mo, Ti which are not specified for EN 10088-1 1.4006.
Can IS 6603 X04Cr17Ni12Mo2Ti be substituted with EN 10088-1 1.4006?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.