Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 6603 X04Cr17Ni12Mo2Ti (IS 6603:2024) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X04Cr17Ni12Mo2Ti is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
IS 6603 X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6603 X04Cr17Ni12Mo2Ti vs EN 10088-1 1.4845 is a 54.6% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 6603 X04Cr17Ni12Mo2Ti:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X04Cr17Ni12Mo2Ti
EN 10088-1 1.4845
Tensile Strength
520-720 MPa
≥515 MPa
Yield Strength
>=205 MPa
≥205 MPa
Elongation
>=40%
≥40%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Not specified
Max Service Temp
Not specified
1100°C continuous
Typical Applications
IS 6603 X04Cr17Ni12Mo2Ti
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
IS 6603 X04Cr17Ni12Mo2Ti specifies P, S, Mo, Ti which are not specified for EN 10088-1 1.4845.
Can IS 6603 X04Cr17Ni12Mo2Ti Be Substituted With EN 10088-1 1.4845?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4845?
IS 6603 X04Cr17Ni12Mo2Ti specifies P, S, Mo, Ti which are not specified for EN 10088-1 1.4845.
Can IS 6603 X04Cr17Ni12Mo2Ti be substituted with EN 10088-1 1.4845?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.