IS 6603 X08Cr17Mn8Cu3N vs EN 10088-1 X8CrMnCuN17-8-3

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 6603 X08Cr17Mn8Cu3N (IS 6603:2024) and EN 10088-1 X8CrMnCuN17-8-3 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X08Cr17Mn8Cu3N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X8CrMnCuN17-8-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X08Cr17Mn8Cu3N vs EN 10088-1 X8CrMnCuN17-8-3 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 6603 X08Cr17Mn8Cu3N:
EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 6603 X08Cr17Mn8Cu3N EN 10088-1 X8CrMnCuN17-8-3
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.10
Si (%) <=2.00 <=2.00
Mn (%) 6.5-9.0 6.5-9.0
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 15.0-18.0 15.0-18.0
Mo (%) <=1.00 <=1.00
Ni (%) <=3.00 <=3.00
N (%) 0.10-0.30 0.10-0.30
Cu (%) 2.00-3.5 2.00-3.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X08Cr17Mn8Cu3N EN 10088-1 X8CrMnCuN17-8-3
Tensile Strength 560-760 MPa Not specified
Yield Strength >=270 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X08Cr17Mn8Cu3N
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X8CrMnCuN17-8-3
Not documented
Can IS 6603 X08Cr17Mn8Cu3N Be Substituted With EN 10088-1 X8CrMnCuN17-8-3?
IS 6603 X08Cr17Mn8Cu3N and EN 10088-1 X8CrMnCuN17-8-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrMnCuN17-8-3 is often considered as a substitute for IS 6603 X08Cr17Mn8Cu3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X08Cr17Mn8Cu3N
0 active listings and RFQs →
EN 10088-1 X8CrMnCuN17-8-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X08Cr17Mn8Cu3N and EN 10088-1 X8CrMnCuN17-8-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X08Cr17Mn8Cu3N be substituted with EN 10088-1 X8CrMnCuN17-8-3?
IS 6603 X08Cr17Mn8Cu3N and EN 10088-1 X8CrMnCuN17-8-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrMnCuN17-8-3 is often considered as a substitute for IS 6603 X08Cr17Mn8Cu3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.