IS 6603 X110Cr17 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6603 X110Cr17 (IS 6603:2024) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X110Cr17 is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 6603 X110Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 6603 X110Cr17 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 60.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6603 X110Cr17:
EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
60.9%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 6603 X110Cr17 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard IS 6603:2024 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 0.07-0.15
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 15.5-17.50
Mo (%) <=0.75 Not specified
Ni (%) <=0.60 12.00-14.50
W (%) Not specified 2.5-3.5
Ti (%) Not specified >=4xC, <=0.80
B (%) Not specified <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X110Cr17 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Hardness <=285 HB Not specified
Condition Soft annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; hardness as printed Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Tensile Strength Not specified 600-800 MPa
Yield Strength Not specified >=390 MPa (0.2 % proof stress)
Elongation Not specified >=25%
Typical Applications
IS 6603 X110Cr17
General purposes, semi-finished products, bars, wire rods and bright bars
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 6603 X110Cr17 Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 6603 X110Cr17 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X110Cr17
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X110Cr17 and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 6603 X110Cr17 specifies Mo which is not specified for IS 1570 (Part 7) 11Cr17Ni13W3TiH. IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for IS 6603 X110Cr17.
Can IS 6603 X110Cr17 be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 6603 X110Cr17 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.