IS 6603 X11Cr19Ni8Mn6N vs EN 10088-3 X11CrNiMnN19-8-6

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 6603 X11Cr19Ni8Mn6N (IS 6603:2024) and EN 10088-3 X11CrNiMnN19-8-6 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X11Cr19Ni8Mn6N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-3 X11CrNiMnN19-8-6 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. IS 6603 X11Cr19Ni8Mn6N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-3 X11CrNiMnN19-8-6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X11Cr19Ni8Mn6N vs EN 10088-3 X11CrNiMnN19-8-6 is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 6603 X11Cr19Ni8Mn6N:
GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 6603 X11Cr19Ni8Mn6N EN 10088-3 X11CrNiMnN19-8-6
Standard IS 6603:2024 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.07-0.15
Si (%) 0.50-1.00 0.50-1.00
Mn (%) 5.0-7.5 5.0-7.5
P (%) <=0.030 <=0.030
S (%) <=0.015 <=0.015
Cr (%) 17.5-19.5 17.5-19.5
Ni (%) 6.5-8.5 6.5-8.5
N (%) 0.20-0.30 0.20-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X11Cr19Ni8Mn6N EN 10088-3 X11CrNiMnN19-8-6
Tensile Strength 750-950 MPa 750-950 MPa
Yield Strength >=340 MPa >=340 MPa
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Elongation Not specified >=35%
Hardness Not specified <=300 HB
Typical Applications
IS 6603 X11Cr19Ni8Mn6N
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-3 X11CrNiMnN19-8-6
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can IS 6603 X11Cr19Ni8Mn6N Be Substituted With EN 10088-3 X11CrNiMnN19-8-6?
IS 6603 X11Cr19Ni8Mn6N and EN 10088-3 X11CrNiMnN19-8-6 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X11CrNiMnN19-8-6 is often considered as a substitute for IS 6603 X11Cr19Ni8Mn6N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X11Cr19Ni8Mn6N
0 active listings and RFQs →
EN 10088-3 X11CrNiMnN19-8-6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X11Cr19Ni8Mn6N and EN 10088-3 X11CrNiMnN19-8-6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X11Cr19Ni8Mn6N be substituted with EN 10088-3 X11CrNiMnN19-8-6?
IS 6603 X11Cr19Ni8Mn6N and EN 10088-3 X11CrNiMnN19-8-6 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X11CrNiMnN19-8-6 is often considered as a substitute for IS 6603 X11Cr19Ni8Mn6N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.