Strong Match — 98.3% match
based on chemical composition and mechanical property overlap.
IS 6911 X02Cr19Ni10 (IS 6911:1992) and ASTM A959 304L (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
IS 6911 X02Cr19Ni10 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while ASTM A959 304L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
IS 6911 X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 304L is defined under ASTM International, originating from United States.
As per chemical composition, IS 6911 X02Cr19Ni10 vs ASTM A959 304L is a 98.3% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 98.3%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6911 X02Cr19Ni10
ASTM A959 304L
Bend Test (180 deg)
Not required
Not specified
Elongation (50 mm, annealed)
>=40%
Not specified
Hardness (annealed, max)
192 HBS, 88 HRB
Not specified
Tensile Strength (annealed)
>=440 MPa
Not specified
Yield Strength (0.2% proof, annealed)
>=180 MPa
Not specified
Typical Applications
IS 6911 X02Cr19Ni10
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
ASTM A959 304L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 6911 X02Cr19Ni10 Be Substituted With ASTM A959 304L?
IS 6911 X02Cr19Ni10 and ASTM A959 304L overlap closely enough on chemistry and mechanical properties that ASTM A959 304L is often considered as a substitute for IS 6911 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6911 X02Cr19Ni10 and ASTM A959 304L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6911 X02Cr19Ni10 be substituted with ASTM A959 304L?
IS 6911 X02Cr19Ni10 and ASTM A959 304L overlap closely enough on chemistry and mechanical properties that ASTM A959 304L is often considered as a substitute for IS 6911 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.